Bend Testing
  • Home
  • Services
  • Bend Testing
  Third Party Inspection     Welding Consultancy     NDT Training Institute     NDT Services & Consultancy     Ultrasonic Testing     Magnetic Particle Testing     Dye Penetrant Testing     Eddy Current Testing     Borescope Inspection     Helium Leak Testing     Oxide Layer Measurement     Ferrite Testing     Infrared Inspection     Radiography Testing     DESTRUCTIVE TESTING SERVICES     Digital Hardness Testing     PMI Services     Corrosion Testing     Metallography Testing     Tensile Testing     Bend Testing     Impact / Izod Testing     Hardness Testing     Manpower Supply and Management     Chemical Analysis (Spectrometry)     Labour Contracting     Staffing Solution     Payroll Services     Recruitment Services  
Bend Test on : Plates, Pipes, Bars

Bend test is mainly done to check ductility of the material and the resistance of the metals to cracking during distortion. From the test maximum bending strength can be determined and the presence of the cracks can easily be revealed. In this test, specimen is subjected to progressive localized overstressing. The test is very simple and requires less time. Conditions for the bend test vary according to various material specifications. Standard sized mandrels are available to bend the specimen to the required angle. The angle which is specified is the internal angle of bend. After bending, the convex surface of the bend is examined for evidence of a crack or surface irregularity. If the specimen fractures, the material has failed the test. When complete fracture does not occur, the criterion for failure is the number and size of cracks or other surface irregularity visible to the unaided eye occurring on the convex surface of the specimen after bending, as specified by the product standard. Any cracks within one thickness of the edge of the specimen are not considered a bend test failure. Cracks occurring in the corners of the bent portion shall not be considered significant unless they exceed the size specified for corner cracks in the product standard.